Build Your Online Product Catalogs?
| Product Name: |
Factory steel material 1.2713/l6/skt4
|
| Supply Ability: |
1000 Ton/Tons per Month |
| Related proudcts |
|
| Specifications |
Length: 2000-5800mm, 2-5.8m ;Width: 60-900mm ;;Thickness: 12-500 |
| Price Term: |
FOB |
| Port of loading: |
Huangshi,any port in China |
| Minimum Order |
1Ton/Tons |
| Unit Price: |
USD2000-3000/Per Ton |
|
ASTM L6 Tool Steel Plate
Equivalent grades GB DIN AISI JIS BS
5CrNiMo 1.2713 L6 SKT4 -
Chemical Composition C Si Mn Cr P/S Ni V Other
0.50-0.60 0.10-0.40 0.65-0.95 1.0-1.2 �.03 1.50-1.80 0.07-0.12 ---
Available size Round Bar Diameter Length
10-380mm 2000-5800mm
Flat Bar Thickness Width Length
12-500mm 60-900mm 2000-5800mm
Surface condition Black surface/ Milled
Annealed hardness HB248MAX
Characteristics Ni alloy die steel with excellent toughness
good through hardening properties
Applications standard materials for forging dies,
hot shear knives, punches,backing plates, die holders, hot punching tools.
Physical Properties Density at 20 °C 7,80 kg/dm3
Thermal expansion between 20 °C and... °C, 10-6 m/(mK)
Thermal conductivity at 20 °C 36,0 W/(m.K)
100 °C 200°C 300 °C 400 °C 500 °C
12.5 13.1 13.4 13.9 14
Heat treatment Annealing 650 - 700 °C
Hardness after annealing Max. 248 HB
Stress relieving Approx. 650 °C
Hot forming 1100 - 850 °C
Hardening 830 - 870 °C or 870 - 900 °C
Quenching media 830 - 870 °C Oil, 870 - 900 °C Air
Hardness after quenching
52 - 58 HRC Oil 44 - 50 HRC, Air
Hardness after tempering
400 °C 500 °C 550 °C 600 °C 400 °C 500 °C 550 °C 600 °C
50 HRC 46 HRC 43 HRC 40 HRC 48 HRC 44 HRC
|
| Company: |
Hubei Joy Imp& Exp Co., Ltd.
|
| Contact: |
Ms. Maggie Yu |
| Address: |
Rm. 3103, No. 18, Yinhe Bay, Jiatai, Huangshi, Hubei, China (Mainland) |
| Postcode: |
|
| Tel: |
86-714-6368760 |
| Fax: |
86-714-6368760 |
| E-mail: |
|
|
|
|
Home